热解对碳纤维/环氧复合材料激光烧蚀的影响

贺敏波, 马志亮, 韦成华, 刘卫平, 吴涛涛

文章导航 > 红外与激光工程 > 2016 > 45(3): 306001-0306001(4)

贺敏波, 马志亮, 韦成华, 刘卫平, 吴涛涛. 热解对碳纤维/环氧复合材料激光烧蚀的影响[J]. 红外与激光工程, 2016, 45(3): 306001-0306001(4). doi: 10.3788/IRLA201645.0306001

引用本文:

He Minbo, Ma Zhiliang, Wei Chenghua, Liu Weiping, Wu Taotao. Influence of pyrolysis on the laser ablation of carbon-fiber/epoxy composite[J]. Infrared and Laser Engineering, 2016, 45(3): 306001-0306001(4). doi: 10.3788/IRLA201645.0306001

Citation:

He Minbo, Ma Zhiliang, Wei Chenghua, Liu Weiping, Wu Taotao. Influence of pyrolysis on the laser ablation of carbon-fiber/epoxy composite[J]. Infrared and Laser Engineering, 2016, 45(3): 306001-0306001(4). doi: 10.3788/IRLA201645.0306001

热解对碳纤维/环氧复合材料激光烧蚀的影响

doi: 10.3788/IRLA201645.0306001

1.
西北核技术研究所激光与物质相互作用国家重点实验室,陕西西安 710024

基金项目:

激光与物质相互作用国家重点实验室基金(SKLLIM1101)

详细信息

作者简介:
贺敏波(1986-),男,工程师,硕士,主要从事激光辐照效应与机理方面的研究。Email:hmb@stu.xjtu.edu.cn

中图分类号: TN249

Influence of pyrolysis on the laser ablation of carbon-fiber/epoxy composite

1.
State Key Laboratory of Laser Interaction with Matter,Northwest Institute of Nuclear Technology,Xi'an 710024,China

摘要: 为研究复合材料的热解问题,设计了氮气流保护条件下的低功率密度辐照实验,获得了不同辐照时间和不同功率密度下碳纤维环氧树脂复合材料层合板的热解规律。实验结果表明:试样质量损失随辐照时间持续呈单调增大趋势,但热烧蚀率却逐渐减小并有稳定趋势;试样质量损失与功率密度呈线性关系;激光功率密度的增加可提高热烧蚀率,但随功率密度的增加,试样热烧蚀率增幅减小并有饱和趋势。
- 激光辐照 /
- 复合材料 /
- 氮气流 /
- 热解
Abstract: In order to study the pyrolysis of composites, an experimental investigation of carbon fiber reinforced epoxy resin composites was carried out. The samples, protected by tangential nitrogen flow, were subjected to a lower power density laser. The influence laws of laser irradiation time and power density on the pyrolysis of composites were obtained and discussed. The results reveal that, along with the laser irradiation time increase, the mass loss of samples increases monotonically while the thermal ablation rate of samples decreases gradually and will tend to be steady. On the other hand, the mass loss of samples is proportional to the laser power density. However, the thermal ablation rate increases significantly at first along with the power density increase, and then slowly since it enters into the glacis.
- laser irradiation /
- composite /
- nitrogen flow /
- pyrolysis

[1]	Kibler K G, Carer H G, Eisenmann J R. Response of graphite composites to laser radiation, FZM-6661[R]. Texas:Materials Research Laboratory, 1977.
[2]	Li Qingyuan. Damage Effects of Vehicles Irradiated by Intense Lasers[M]. Beijing:China Astronautic Press, 2012:8. (in Chinese)
[3]	Guo Yalin, Liang Guozheng, Qiu Zhiming, et al. Effect of laser parameters on mass ablative rate of carbon fiber reinforced composite[J]. Acta Materiae Compositae Sinica, 2006, 23(5):84-88. (in Chinese)
[4]	Chen Bo, Wan Hong, Mu Jingyang, et al. Ablative mechanism of carbonfiber/epoxy composite irradiated by repetition frequency laser[J]. High Power Laser and Particle Beams, 2008, 20(4):547-552. (in Chinese)
[5]	Huang Yongguang, Liu Shibing, Long Lianchun, et al. Mass ablation characteristics of carbon fiber composite irradiated by Nd:YAG laser[J]. Acta Materiae Compositae Sinica, 2009, 26(1):118-122. (in Chinese)
[6]	Li Yadi, Wu Ping, Ma Ximei, et al. The tests of carbon fiber/epoxy laminated composites under continuous laser irradiation[J]. Fiber Composites, 2010, 21(2):21-24. (in Chinese)
[7]	Wan Hong, Hu Kaiwei, Mu Jingyang, et al. Damage analysis of fiber reinforced resin matrix composites irradiated by CW laser[J]. High Power Laser and Particle Beams, 2008, 20(1):6-10. (in Chinese)
[8]	Mu Jingyang, Wan Hong, Bai Shuxin. Thermal ablation law of cured epoxy under long pulse laser irradiation[J]. Power Laser and Particle Beam, 2008, 20(1):36-40. (in Chinese)
[9]	Chen Mingshun, Jiang Houman, Jiao Luguang, et al. Damage of carbon fiber reinforced resin matrix composite subjected to laser and tangential gas flow loading[J]. Acta Materiae Compositae Sinica, 2013, 30(3):56-62. (in Chinese)
[10]	Chen Mingshun, Jiang Houman, Liu Zejin. MSPH method applied to simulate the irradiation effect of resin composites irradiated by laser[J]. Infrared and Laser Engineering, 2012, 41(4):889-894. (in Chinese)

[1]	李倩靓, 张润华, 何宗泰, 张骆, 杨奇彪, 夏建英, 刘顿. 脉冲和连续模式下玻璃纤维复合材料激光脱漆技术研究(特邀) . 红外与激光工程, 2023, 52(2): 20220836-1-20220836-12. doi: 10.3788/IRLA20220836
[2]	温佳起, 卞进田, 李欣, 孔辉, 郭磊, 吕国瑞. 激光干扰和损伤CMOS图像传感器研究进展（特邀） . 红外与激光工程, 2023, 52(6): 20230269-1-20230269-15. doi: 10.3788/IRLA20230269
[3]	周伟静, 文明, 常浩, 陈一夫, 姬刚, 马英杰, 简智龙, 廖雨杰. 皮秒脉冲激光辐照太阳能电池损伤特性实验研究（特邀） . 红外与激光工程, 2023, 52(2): 20210870-1-20210870-10. doi: 10.3788/IRLA20210870
[4]	王轩, 赵晨起. 弹载光学系统复合材料支撑结构低热膨胀优化 . 红外与激光工程, 2023, 52(5): 20220742-1-20220742-11. doi: 10.3788/IRLA20220742
[5]	张晓腾, 李泽文, 周义青, 沈中华. 在亚音速气流作用下连续激光辐照铝合金的穿孔效应 . 红外与激光工程, 2022, 51(2): 20210883-1-20210883-10. doi: 10.3788/IRLA20210883
[6]	梁晓琳, 周松青, 周玲, 包本刚. 激光辐照条件下光学相机像质评价方法研究 . 红外与激光工程, 2022, 51(10): 20211120-1-20211120-7. doi: 10.3788/IRLA20211120
[7]	杨正伟, 赵志彬, 高建国, 寇光杰, 张炜. 热固性/热塑性复合材料分层损伤红外热波检测能力评估 . 红外与激光工程, 2021, 50(S2): 20210304-1-20210304-9. doi: 10.3788/IRLA20210304
[8]	李欣, 陈永, 李伟仙, 李洋洋, 郑磊, 吴思进. 投影辅助的数字剪切散斑干涉扫描检测技术 . 红外与激光工程, 2021, 50(8): 20210509-1-20210509-8. doi: 10.3788/IRLA20210509
[9]	暴丽霞, 乔小晶, 杨铭. 一锅水热法制备炭-铁磁体复合材料及红外消光性能研究（特约） . 红外与激光工程, 2020, 49(7): 20201020-1-20201020-6. doi: 10.3788/IRLA20201020
[10]	胡朝斌, 金星, 常浩. 空间翻滚目标激光消旋概念及天基应用分析 . 红外与激光工程, 2020, 49(8): 20200203-1-20200203-9. doi: 10.3788/IRLA20200203
[11]	陈一夫, 常浩, 周伟静, 于程浩. 脉冲激光辐照太阳能电池响应及光电转化影响 . 红外与激光工程, 2020, 49(S1): 20200262-20200262. doi: 10.3788/IRLA20200262
[12]	王震, 杨正伟, 陶胜杰, 朱海波, 张炜. 基于移相技术的含缺陷复合材料锁相热波检测 . 红外与激光工程, 2019, 48(S2): 60-67. doi: 10.3788/IRLA201948.S204002
[13]	王强, 胡秋平, 邱金星, 裴翠祥, 刘铭, 李欣屹, 周洪斌. 航空复合材料内部缺陷差动式激光红外热成像检测 . 红外与激光工程, 2019, 48(5): 504003-0504003(7). doi: 10.3788/IRLA201948.0504003
[14]	黄战华, 陈勃昊, 刘堃, 蔡怀宇, 张尹馨. 长波红外激光目标仿真中拖尾现象的消除方法 . 红外与激光工程, 2019, 48(7): 704004-0704004(6). doi: 10.3788/IRLA201948.0704004
[15]	刘孝谦, 骆芳, 杜琳琳, 陆潇晓. 激光能量密度对原位生成纳米石墨的影响 . 红外与激光工程, 2019, 48(5): 506004-0506004(8). doi: 10.3788/IRLA201948.0506004
[16]	阚宝玺, 杨超, 卞贺明, 唐才杰, 黄建业, 王学锋, 孟庆平, 孙维, 高行素. 植入式光纤光栅应变传感器的湿度影响 . 红外与激光工程, 2018, 47(S1): 92-98. doi: 10.3788/IRLA201847.S122007
[17]	谢运涛, 张玉钧, 王玺, 孙晓泉. 基于微通道板的像增强器增益饱和效应研究 . 红外与激光工程, 2017, 46(10): 1003005-1003005(6). doi: 10.3788/IRLA201750.1003005
[18]	张东来, 李小将, 杨业伟. 激光辐照飞行靶三维温度场数值模拟 . 红外与激光工程, 2014, 43(9): 2883-2888.
[19]	岳丽清, 张继友. 复合材料在热真空下的尺寸稳定性测试方法 . 红外与激光工程, 2014, 43(11): 3713-3717.
[20]	李君神, 赵国民, 焦路光, 袁春, 陈敏孙. 切向气流作用下激光对薄铝板辐照效应的初步研究 . 红外与激光工程, 2013, 42(11): 2962-2966.

点击查看大图

计量

文章访问数: 326
HTML全文浏览量: 38
PDF下载量: 164
被引次数: 0

热解对碳纤维/环氧复合材料激光烧蚀的影响

doi: 10.3788/IRLA201645.0306001

1. 西北核技术研究所激光与物质相互作用国家重点实验室,陕西西安 710024

作者简介:
贺敏波(1986-),男,工程师,硕士,主要从事激光辐照效应与机理方面的研究。Email:hmb@stu.xjtu.edu.cn

收稿日期: 2015-07-05
修回日期: 2015-08-13
刊出日期: 2016-03-25

基金项目:

激光与物质相互作用国家重点实验室基金(SKLLIM1101)

中图分类号: TN249

关键词:

摘要: 为研究复合材料的热解问题,设计了氮气流保护条件下的低功率密度辐照实验,获得了不同辐照时间和不同功率密度下碳纤维环氧树脂复合材料层合板的热解规律。实验结果表明:试样质量损失随辐照时间持续呈单调增大趋势,但热烧蚀率却逐渐减小并有稳定趋势;试样质量损失与功率密度呈线性关系;激光功率密度的增加可提高热烧蚀率,但随功率密度的增加,试样热烧蚀率增幅减小并有饱和趋势。