热障涂层厚度激光透射法红外热波检测技术研究

李永君 肖俊峰 朱立春 张炯 高斯峰 唐文书 南晴

李永君, 肖俊峰, 朱立春, 张炯, 高斯峰, 唐文书, 南晴. 热障涂层厚度激光透射法红外热波检测技术研究[J]. 红外与激光工程, 2017, 46(7): 704003-0704003(5). doi: 10.3788/IRLA201746.0704003
引用本文: 李永君, 肖俊峰, 朱立春, 张炯, 高斯峰, 唐文书, 南晴. 热障涂层厚度激光透射法红外热波检测技术研究[J]. 红外与激光工程, 2017, 46(7): 704003-0704003(5). doi: 10.3788/IRLA201746.0704003
Li Yongjun, Xiao Junfeng, Zhu Lichun, Zhang Jiong, Gao Sifeng, Tang Wenshu, Nan Qing. Research on detection of thickness of thermal barrier coating by laser transmission infrared thermal wave method[J]. Infrared and Laser Engineering, 2017, 46(7): 704003-0704003(5). doi: 10.3788/IRLA201746.0704003
Citation: Li Yongjun, Xiao Junfeng, Zhu Lichun, Zhang Jiong, Gao Sifeng, Tang Wenshu, Nan Qing. Research on detection of thickness of thermal barrier coating by laser transmission infrared thermal wave method[J]. Infrared and Laser Engineering, 2017, 46(7): 704003-0704003(5). doi: 10.3788/IRLA201746.0704003

热障涂层厚度激光透射法红外热波检测技术研究

doi: 10.3788/IRLA201746.0704003
基金项目: 

国家自然科学基金(51501151);华能集团总部科技项目(HNKJ15-H05)

详细信息
    作者简介:

    李永君(1987-),男,工程师,硕士,主要从事激光与红外检测技术方面的研究。Email:lee19870914@163.com

    通讯作者: 肖俊峰(1974-),男,研究员,硕士,主要从事汽轮机及燃气轮机相关技术方面的研究。Email:xiaojunfeng@tpri.com.cn
  • 中图分类号: TN219

Research on detection of thickness of thermal barrier coating by laser transmission infrared thermal wave method

  • 摘要: 在传热学的基础上建立涂层试样的一维热传导模型,确立了涂层厚度与表面温度差值-帧数直线的斜率、截距以及涂层热扩散率之间的定量关系。以不同厚度的热障涂层试样为例,采用新型脉冲激光透射法激励,对热像仪采集到的不同激励功率下涂层表面温度差值-帧数曲线线性拟合,求得拟合直线的斜率和截距值,最后计算得到热障涂层厚度值,结果表明:激光透射法红外热波检测技术能很好地应用于热障涂层厚度的快速、精确、非接触检测。
  • [1] Fang Xufei, Zhang Guobing, Feng Xue. Performance of TBCs system due to the different thickness of top ceramic layer[J]. Ceramics International, 2015, 41(2):2840-2846.
    [2] Lu Z, Myoung S W, Kim E H, et al. Microstructure evolution and thermal durability with coating thickness in APS thermal barrier coatings[J]. Materials Today:Proceedings, 2014, 1(1):35-43.
    [3] Moskal G, Witala B, Rozmyslowska A. Metallographic preparation of the conventional and new TBC layers[J]. Archives of Materials Science and Engineering, 2009, 39(1):53-60.
    [4] Li Yong, Chen Zhenmao, Mao Ying, et al. Quantitative evaluation of thermal barrier coating based on eddy current technique[J]. NDT E International, 2012, 50(1):29-35.
    [5] Ma Zhiyuan, Zhao Yang, Luo Zhongbing, et al. Ultrasonic characterization of thermally grown oxide in thermal barrier coating by reflection coefficient amplitude spectrum[J]. Ultrasonics, 2014, 54(4):1005-1009.
    [6] Zhang Jinyu, Meng Xiangbing, Yang Zhengwei, et al. Numerical simulation and analysis of lock-in thermography for thickness measurement of coating[J]. Infrared and Laser Engineering, 2015, 44(1):6-11. (in Chinese)
    [7] Chen Lin, Yang Li, Fan Chunli, et al. Quantitative identification of coating thickness and debonding defects of TBC by pulse technology[J]. Infrared and Laser Engineering, 2015, 44(7):2050-2056. (in Chinese)
    [8] Hong Wenqing, Yao Libin, Ji Rongbin, et al. A super-frame processing method for infrared image based on accumulation of different integration time frame[J]. Optics and Precision Engineering, 2016, 24(6):1490-1501. (in Chinese)
    [9] Zhao Shibin, Wang Huaming, Wu Naiming, et al. Nondestructive testing of the fatigue properties of air plasma sprayed thermal barrier coatings by pulsed thermography[J]. Thermal Methods, 2015, 51(7):445-456.
    [10] Shepard Steven M, Hou Yulin, Lhota James R, et al. Thermographic measurement of thermal barrier coating thickness[C]//Proceedings of the SPIE, 2005, 5782(1):407-410.
    [11] Kumar M Mahesh, Vikrant K S, Swamy M, et al. Theoretical estimation of thickness variation in thermal barrier coatings by using pulse phase thermograph[C]//11th International Conference on Quantitative Infrared Thermography, 2012, 6(1):11-14.
    [12] Wang Lijun, Peng Hangyu, Zhang Jun. Advance on high power diode laser coupling[J]. Chinese Opitcs, 2015, 8(4):517-519. (in Chinese)
    [13] Guo Xiantao, Huang Teng, Sheng Yueqian. Self-calibration of terrestrial laser scanner based on stochastic inner constraint information of estimated parameters[J]. Optics and Precision Engineering, 2016, 24(6):1319-1327. (in Chinese)
    [14] Dong Lei, Liu Xinyue, Chen Hao. Properties of pulse single-frequency laser and extra-cavity double frequency green laser[J]. Chinese Opitcs, 2015, 8(5):800-806. (in Chinese)
    [15] Grzgorz Ptaszek, Cawley Peter, Almond Darryl, et al. Artificial disbands for calibration of transient thermography inspection of thermal barrier coatings systems[J]. NDT E International, 2012, 45(1):71-78.
    [16] Zhao Y, Ma Zhenyue, Lin Li, et al. A method for ultrasonic characterization of density, thickness and velocity of homogeneous coating[J]. Materials Science Forum, 2011, 675(677):1217-1220.
  • [1] 王云哲, 张鲁薇, 邵俊峰, 曲卫东, 康华超, 张引.  脉冲激光对石英基底Ta2O5/SiO2滤光膜的损伤效应研究 . 红外与激光工程, 2023, 52(3): 20220482-1-20220482-9. doi: 10.3788/IRLA20220482
    [2] 何涛, 沈中华, 陈飞, 陈力.  脉冲红外热波用于半透明涂层厚度测量 . 红外与激光工程, 2022, 51(2): 20210890-1-20210890-8. doi: 10.3788/IRLA20210890
    [3] 周国清, 谭逸之, 周祥, 李伟豪, 李先行, 林港超, 胡皓程, 张烈平, 农学勤, 杨家志.  波长1 064 nm和532 nm脉冲激光大动态范围能量的测试方法及实验 . 红外与激光工程, 2021, 50(S2): 20200417-1-20200417-8. doi: 10.3788/IRLA20200417
    [4] 刘颖韬, 许路路, 何方成, 李硕宁, 杨党纲.  环境因素对闪光灯激励红外热成像外场检测的影响 . 红外与激光工程, 2021, 50(12): 20210711-1-20210711-8. doi: 10.3788/IRLA20210711
    [5] 安恒, 李得天, 文轩, 张晨光, 王鷁, 马奎安, 李存惠, 薛玉雄, 杨生胜, 曹洲.  高速PWM单粒子瞬态效应脉冲激光模拟试验研究 . 红外与激光工程, 2020, 49(8): 20190533-1-20190533-7. doi: 10.3788/IRLA20190533
    [6] 高磊, 李慧芸.  基于选择性激光改性的双陶瓷层热障涂层界面增韧方法 . 红外与激光工程, 2020, 49(1): 0105005-0105005(8). doi: 10.3788/IRLA202049.0105005
    [7] 周旋风, 陈前荣, 王彦斌, 朱荣臻, 李华, 任广森.  脉冲激光辐照CMOS相机的图像间断现象及机理 . 红外与激光工程, 2019, 48(3): 306002-0306002(6). doi: 10.3788/IRLA201948.0306002
    [8] 安恒, 张晨光, 杨生胜, 薛玉雄, 王光毅, 王俊.  SiGeBiCMOS线性器件脉冲激光单粒子瞬态效应研究 . 红外与激光工程, 2019, 48(3): 320001-0320001(7). doi: 10.3788/IRLA201948.0320001
    [9] 林正国, 金星, 常浩.  脉冲激光大光斑辐照空间碎片冲量耦合特性研究 . 红外与激光工程, 2018, 47(12): 1243001-1243001(6). doi: 10.3788/IRLA201847.1243001
    [10] 陈杉杉, 张合, 徐孝彬.  脉冲激光周向探测地面目标捕获建模与仿真 . 红外与激光工程, 2018, 47(2): 206001-0206001(11). doi: 10.3788/IRLA201847.0206001
    [11] 王惠, 党凡阳, 张荣达, 明月, 范志刚.  半球形整流罩厚度对气动热辐射的影响 . 红外与激光工程, 2018, 47(12): 1204002-1204002(6). doi: 10.3788/IRLA201847.1204002
    [12] 唐进迎, 雷武虎, 任晓东, 张坤, 张明鑫.  星载荷热控制辐冷板激光致热计算分析 . 红外与激光工程, 2018, 47(12): 1243002-1243002(8). doi: 10.3788/IRLA201847.1243002
    [13] 张月, 王睿, 杨海峰.  线阵碲镉汞探测器对纳秒脉冲激光的反常响应规律及机理 . 红外与激光工程, 2017, 46(10): 1003003-1003003(7). doi: 10.3788/IRLA201748.1003003
    [14] 张震, 徐作冬, 程德艳, 师宇斌, 张检民.  FT-CCD的纳秒脉冲激光毁伤效应 . 红外与激光工程, 2017, 46(10): 1003001-1003001(5). doi: 10.3788/IRLA201746.1003001
    [15] 金星, 常浩, 叶继飞.  超短脉冲激光烧蚀冲量耦合测量方法 . 红外与激光工程, 2017, 46(3): 329002-0329002(7). doi: 10.3788/IRLA201746.0329002
    [16] 郭伟, 董丽虹, 王海斗, 徐雅薇, 徐滨士.  基于小波分解的热波相位特征提取及喷涂层厚度评价 . 红外与激光工程, 2017, 46(9): 904003-0904003(7). doi: 10.3788/IRLA201746.0904003
    [17] 华浩然, 袁丽华, 邬冠华, 吴伟.  透射法的红外热波缺陷定量检测研究 . 红外与激光工程, 2016, 45(2): 204007-0204007(6). doi: 10.3788/IRLA201645.0204007
    [18] 张长桃, 张朝阳, 蔡明霞, 丁伟, 毛卫平, 徐宇蓝.  脉冲激光热力冲击效应对电沉积的作用 . 红外与激光工程, 2015, 44(1): 65-70.
    [19] 陈林, 杨立, 范春利, 石宏臣, 赵小龙.  基于相位的热障涂层厚度及其脱粘缺陷红外定量识别 . 红外与激光工程, 2015, 44(7): 2050-2056.
    [20] 唐庆菊, 王扬, 刘俊岩, 秦雷, 龚金龙, 齐立涛.  耐热合金涂层结构板材内部缺陷的脉冲红外热成像检测 . 红外与激光工程, 2013, 42(7): 1685-1690.
  • 加载中
计量
  • 文章访问数:  351
  • HTML全文浏览量:  45
  • PDF下载量:  90
  • 被引次数: 0
出版历程
  • 收稿日期:  2016-11-05
  • 修回日期:  2016-12-03
  • 刊出日期:  2017-07-25

热障涂层厚度激光透射法红外热波检测技术研究

doi: 10.3788/IRLA201746.0704003
    作者简介:

    李永君(1987-),男,工程师,硕士,主要从事激光与红外检测技术方面的研究。Email:lee19870914@163.com

    通讯作者: 肖俊峰(1974-),男,研究员,硕士,主要从事汽轮机及燃气轮机相关技术方面的研究。Email:xiaojunfeng@tpri.com.cn
基金项目:

国家自然科学基金(51501151);华能集团总部科技项目(HNKJ15-H05)

  • 中图分类号: TN219

摘要: 在传热学的基础上建立涂层试样的一维热传导模型,确立了涂层厚度与表面温度差值-帧数直线的斜率、截距以及涂层热扩散率之间的定量关系。以不同厚度的热障涂层试样为例,采用新型脉冲激光透射法激励,对热像仪采集到的不同激励功率下涂层表面温度差值-帧数曲线线性拟合,求得拟合直线的斜率和截距值,最后计算得到热障涂层厚度值,结果表明:激光透射法红外热波检测技术能很好地应用于热障涂层厚度的快速、精确、非接触检测。

English Abstract

参考文献 (16)

目录

    /

    返回文章
    返回