Effects of hot isostatic pressing on microstructure and tensile properties of direct laser deposited Ti60 alloys
-
摘要: 利用激光直接沉积技术成形Ti60 合金,研究热等静压双重退火对激光直接沉积Ti60 合金缺陷、组织及拉伸性能的影响。结果表明:激光直接沉积Ti60 合金存在气孔和未熔合两种缺陷,经热等静压处理后,气孔和尺寸较小的未熔合缺陷消除;沉积态试样底部和中部为柱状晶,顶部为等轴晶,显微组织为魏氏组织,由板条和板条间组成;经热等静压双重退火处理后,晶界消融,大部分原始晶界消失,板条粗化,长宽比减小,显微组织变为网篮组织;与锻件相比,沉积态试样拉伸强度较高,塑性较低,经热等静压双重退火处理后,其塑性达到了锻件标准。Abstract: Ti60 alloys were fabricated by using direct laser deposition (DLD) technology and it was studied that the effects of hot isostatic pressing (HIP) on defects, microstructure and tensile properties of the DLD Ti60 alloys. The results show that there are two typical kinds of defects in the DLD Ti60 alloys, which are pores and lack of fusion. After HIP treatment, pores and the small size of lack of fusion are eliminated. There are columnar crystals at the bottom and the middle of the as-deposited specimens, but at the top of the specimens are equiaxed grains. The microstructure is widmanstatten structure, which is composed of alpha laths and beta between the laths. After HIP and double annealing treatment, the grain boundary alpha melting, the most of the original beta grain boundaries disappear, alpha laths coarsening, the length-width ratio decreases, and the microstructure becomes basket-weave microstructure. Compared with the forgings, the as-deposited specimens have a high tensile strength with a low plasticity, after HIP and double annealing treatment, the plasticity of the as-deposited specimens exceeds the standards of the forgings.
-
Key words:
- additive manufacturing /
- direct laser deposition /
- titaniumalloy /
- Ti60 /
- hot isostatic pressing
-
[1] Zhao Yongqing. Current situation and development trend of titanium alloy [J ]. Materials China, 2010 (5): 1-8. (in Chinese) [2] [3] [4] Wei Shouyong, Shi Weimin, Wang Dingchun, et al. Microstructure and mechanical properties of high temperature titanium alloy Ti60 at 600℃ [J]. The Chinese Journal of Nonferrous Metal, 2010(S1): 801-806. (in Chinese) [5] Chen Jing, Yang Haiou, Yang Jian, et al. Technical study on the laser rapid forming of Rene95 and TC4 titanium alloy[J]. Journal of Aeronautical Materials, 2003, 33 (10): 100-103. (in Chinese) [6] [7] [8] Huang Weidong, Lin Xin. Research progress in laser solid forming of high performance metallic component [J]. Materials China, 2010, 29(6): 12-27. (in Chinese) [9] [10] Wang Kun, Meng Mu, Wang Huaming. Effect of heat treatment and laser multi-track overlapping on microstructure of a laser melting deposition TC18 titanium alloy [J]. Infrared and Laser Engineering, 2010, 39(3): 521-525. (in Chinese) [11] Yuan Hong, Fang Yanli, Wang Huaming. Influence of heat treatment on microstructure and compressive property of laser melting deposited TA15 titanium alloy [J]. Infrared and Laser Engineering, 2010, 39(4): 746-750. (in Chinese) [12] [13] [14] Kobryn P A, Moore E H, Semiatin S L. The effect of laser power and traverse speed onmicrostructure, porosity, and build height in laser-deposited Ti-6Al-4V [J ]. Scripta Materialia, 2000, 43(4): 299-305. [15] Wu X, Liang J, Mei J, et al. Microstructures of laser-deposited Ti-6Al-4V[J]. Materials Design, 2004, 25(2): 137-144. [16] [17] Majumdar J D, Pinkerton A, Liu Z, et al. Microstructure characterisation and processoptimization of laser assisted rapid fabrication of 316L stainless steel [J]. Applied Surface Science, 2005, 247(1): 320-327. [18] [19] Zhang Fengying, Chen Jing, Tan Hua, et al. The study on defect forming mechanism of titanium alloy during laser rapid forming [J]. Rare Metal Materials and Engineering, 2007, 36(2): 211-215. (in Chinese) [20] [21] [22] Li Huaixue, Gong Shuili, Fei Qunxing. Effect of hot isostatic pressing on microstructure and tensile properties of direct laser deposited BT6 alloys [J]. Applied Laser, 2011, 31(1): 45-49. (in Chinese) [23] [24] Wang Bin, Zhang Shuquan, Wang Huaming. Rapidly solidified microstructure of Ti60 alloy produced by laser rapid forming process [J]. Transactions of Materials and Heat Treatment, 2008, 29(6): 86-92. (in Chinese) [25] Sun Jingchao, Zhang Yongzhong, Huang Can, et al. Microstructure and high temperature tensile properties of laser direct deposited Ti60 alloy and TiCP/Ti60 composites[J]. Chinese Journal of Lasers, 2011, 38 (3): 103-108. (in Chinese) [26] [27] Zhang Fang, Chen Jing, Xue Lei, et al. Microstructure and mechanical properties of laser solid formed Ti60 alloy [J]. Rare Metal Materials and Engineering, 2010, 39 (3): 452-456. (in Chinese) -
点击查看大图
计量
- 文章访问数: 413
- HTML全文浏览量: 95
- PDF下载量: 171
- 被引次数: 0
下载: