Effects of damaged appearance of coatings on its conditioning during laser conditioning
- Received Date: 2012-05-07
- Rev Recd Date:
2012-06-13
- Publish Date:
2013-01-25
-
Abstract
The damage threshold can increase 2-3 times through laser conditioning optical component using the subthreshold laser energy. In the process, it will make the optical component produce damage inevitably, if the damage does not affect the optical performance, which is acceptable in principle. In this paper, the S-on-1 LIDT of hafnia silica multilayer high reflective coatings was introduced firstly. Experimentally, the damage process of optical coatings during laser conditioning was studied. At the same time, the laser damage appearance that affected the optical capability and LIDT of coatings was analyzed. The result is, with the film system of G/(HL)11H2L/A, after laser conditioning for the HfO2/SiO2 multilayer HR coatings, the destroyed of outermost SiO2 coating can not affect its spectrum performance. Reversely, the LIDT of coatings is enhanced sharply because removing the nodula in the next HfO2 coating.
-
References
|
[1]
|
Bertussi B, Damiani D, Pommies M, et al. Laser conditioning of KDP crystals using excimer and Nd:YAG lasers[C]//SPIE, 2006, 6403: 457-463. |
|
[2]
|
|
|
[3]
|
Damiani D, Piombini H, Plessis D, et al. Excimer laser conditioning of KDP: influence of the laser parameters and crystal orientation on the laser damage threshold[C]//SPIE, 2005, 5647: 290-298. |
|
[4]
|
|
|
[5]
|
Kozlowski M R, Wolfe C R, Staggs M C, et al. Large area laser conditioning of dielectric thin film mirrors[C]//SPIE, 1989, 1438: 376-390. |
|
[6]
|
|
|
[7]
|
Stolz C J, Sheehan L M, Maricle S M, et al. A study of laser conditioning methods of hafnia silica multilayer mirrors[C]//SPIE, 1998, 3264: 105-112. |
|
[8]
|
|
|
[9]
|
|
|
[10]
|
Wolfe C R, Kozlowski M R, Campbell J H, et al. Laser conditioning of optical thin films[C]//SPIE, 1989, 1438: 360-375. |
|
[11]
|
Zhao Qiang, Qiu Hong, Liu Ye, et al. Study of laser conditioning of optical coatings with small spot scanning[J]. Acta Optica Sinica, 1999, 19(8): 1105-1109. (in Chinese) |
|
[12]
|
|
|
[13]
|
Campbell J H, Hawley-Fedder R A, Stolz C J. NIF optical materials and fabrication technologies: An overview[C]// SPIE, 2004, 5341: 84-101. |
|
[14]
|
赵强, 裘弘, 刘晔, 等. 光学薄膜的小光斑扫描激光预处理研究[J]. 光学学报, 1999, 19(8): 1105-1109. |
|
[15]
|
|
|
[16]
|
Dai Fu, Yang Liming. Study on laser energy that irradiate the defect during laser conditioning process[J]. High Power Laser and Particle Beams, 2012, 24(6): 1385-1390. (in Chinese) |
|
[17]
|
|
|
[18]
|
Fan Zhengxiu, Wu Zhouling, Tang Xuefei. Repeat-rate-laser induced damage in optical coatings[J]. Chinese Journal of Lasers, 1994, 21(9): 734-738. (in Chinese) |
|
[19]
|
Schildbach M, Chase L L, Hamza A V. Investigation of neutral atom and ion emission during laser conditioning of multilayer HfO2/SiO2 coatings[C]//SPIE, 1990, 1441: 287-293. |
|
[20]
|
|
|
[21]
|
代福, 杨李茗. 激光预处理中缺陷的激光能量覆盖研究[J]. 强激光与粒子束, 2012, 24(6): 1385-1390. |
|
[22]
|
|
|
[23]
|
|
|
[24]
|
范正修, 吴周令, 汤雪飞. 重复率激光对光学薄膜的破坏[J]. 中国激光, 1994, 21(9): 734-738. |
|
[25]
|
|
-
-
Proportional views
-
DownLoad: